Effect of nitrogen content on physical properties of glass fiber reinforced polyamide 6 prepared by microcellular injection molding

The aim of the study was to determine the effect of the amount of nitrogen dosed in supercritical state to polymer melt on structure and physical properties of large-scale molded pieces from polyamide PA 6 GF30, obtained in the process of microcellular injection molding with gas dosage using MuCell® method. Apart from the reduction of the density at a level of about 15 % for samples with the highest nitrogen content, the increase of the impact resistance of samples PA 6 GF30 was observed. The other investigated mechanical properties were maintained at a good level.

Określano wpływ ilości azotu, dozowanego w stanie nadkrytycznym do stopu polimerowego, na strukturę i właściwości wielkogabarytowych wyprasek wytworzonych w procesie wtryskiwania mikroporującego metodą MuCell® z poliamidu 6 zawierającego 30 % mas. krótkich włókien szklanych (PA6 GF30). Stwierdzono zmniejszenie o ok. 15 % gęstości próbek z największą zawartością azotu oraz wzrost udarności otrzymanych wyprasek PA6 GF30, przy zachowaniu na dobrym poziomie pozostałych właściwości wytrzymałościowych.