The Study Of The Impact Of Surface Preparation Methods Of Inconel 625 And 718 Nickel-Base Alloys On Wettability By BNi-2 And BNi-3 Brazing Filler Metals

The article discusses the impact of surface preparation method of Inconel 625 and 718 nickel-base alloys in the form of sheets on wettability of the surface. The results of the investigations of surface preparation method (such as nicro-blasting, nickel plating, etching, degreasing, abrasive blasting with grit 120 and 220 and manually grinding with grit 120 and 240) on spreading of BNi-2 and BNi-3 brazing filler metals, widely used in the aerospace industry in high temperature vacuum brazing processes, are presented. Technological parameters of vacuum brazing process are shown. The macro- and microscopic analysis have shown that nicro-blasting does not bring any benefits of wettability of the alloys investigated.

W artykule omówiono wpływ metody przygotowania powierzchni na zwilżalność blach ze stopów niklu Inconel 625 oraz 718. Przedstawiono wyniki badań wpływu metod przygotowania powierzchni (technologii nicro-blasting, niklowania galwanicznego, trawienia, odtłuszczania, obróbki strumieniowo ściernej ścierniwem o granulacji 120 oraz 220, a także ręcznego szlifowania papierem ściernym o ziarnistości 120 oraz 240) na rozpływność dwóch gatunków lutu BNi-2 oraz BNi-3, które są powszechnie stosowane w przemyśle lotniczym podczas procesów wysokotemperaturowego lutowania w próżni. Podano parametry technologiczne procesu lutowania próżniowego. Wyniki badań makro- i mikroskopowych wykazały, że nicro-blasting nie wpływa korzystnie na zwilżalność badanych stopów.